| Model Index | FR-245 |
ABS300 | ABS302 | ABS303 |
| Product name | Bromo-triazine | ABS general flame retardant masterbatch | ABS efficient flame retardant masterbatch | ABS high liquidity flame retardant masterbatch |
| Appearance | White powder | White spherical granule | White spherical granule | White cylindrical granule |
| Content of fire retardant % | Bromine content ≥67 | ≥80 | ≥88 | ≥75 |
| Density g/cm3 | 2.50 | 1.7 | 2.05 | 1.8 |
| Melting index 230℃, 10kg | - | 4.6 | 4.05 | 50(200℃,5kg) |
| Double-screw temperature ℃ | ≤200 | ≤180 | ≤200 | ≤200 |
| Injection temperature ℃ | ≤220 | ≤200 | ≤220 | ≤220 |
| No. | A | B | C | D | E | ABS raw materials |
| ABS | 82 | 82 | 80 | 77 | 77 | - |
| DBDPE | 12 | - | - | - | - | - |
| FR-245 | - | - | - | 16 | - | - |
| Sb2O3 | 4 | - | - | 4 | - | - |
| Additive + others | 2 | - | - | 3 | - | - |
| ABS300 | - | 18 | - | - | - | - |
| ABS302 | - | - | 18 | - | - | - |
| ABS303 | - | - | - | - | 23 | - |
| UL94/3.2mm | V0 | V0 | V0 | V0 | V0 | Burning |
| Notched impact (23℃)KJ/m2 | 8.5 | 9.9 | 9.0 | 10.5 | 12.9 | 25 |
| Tensile strength MPa | 39.3 | 40 | 42.5 | 47.9 | 42.2 | 51 |
| Elongation at break % | 18.6 | 36.6 | 30.4 | 30.3 | 36.2 | 40 |
| Bending strength MPa | 58 | 61.5 | 66.2 | 73.7 | 66.2 | 77 |
| Flexural modulus MPa | 2491 | 1893 | 1900 | 2196 | 1910 | 2518 |
| Model | Product advantages |
| ABS300 | It is the most cost-effective; with good cold resistance, UV resistance, no precipitation, good performance, excellent dispersion. 18% shares are added, 3.2 mm flame retarding is up to UL94V0. 22% shares are added, and it is qualified in 750 ℃ glowing filament tests. |
| ABS302 | It is suitable for modification granulation products with slow extrusion speed and high processing temperature; It is characterized by low dosage, higher temperature resistance, UV resistance and no precipitation. it is qualified in 750 ℃ glowing filament tests. |
| ABS303 | It has excellent liquidity and whiteness. ABS carrier is adopted, the obtained finished products are characterized by excellent color match, bright and clean appearance, low influence on material performance, better resistance to UV, no frost and no precipitation, it is suitable for large products and thin-wall products, which is easier to inject sufficiently. It is qualified in 750 ℃ glowing filament test. |